【供应热线:13528622273】PA66 CM3001-N日本东丽阻燃级尼龙树脂物性参数
台湾南亚PA66 6212GA FNC1尼龙塑胶颗粒
以下PA66 CM3001-N日本东丽阻燃级尼龙树脂物性参数仅供参考,请以实际操作为准;
PA66 CM3001-N|东丽尼龙树脂|阻燃尼龙材料物性|日本东丽尼龙树脂|
尼龙材料价格
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
无水 | 2.5%水 | |||||
基本性能 | 吸水率 | 23℃,24小时 | ASTM D-570 | 1.2 | - | % |
物理性能 | 比重 | --- | ASTM D-792 | 1.13-1.14 | - | --- |
泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 8 | - | mg/1000次 | |
机械性能 | IZOD冲击强度 | 23℃,V缺口1/2 | --- | 5 | 28 | kg.cm/cm |
IZOD冲击强度 | 23℃,无缺口1/8 | --- | 无断裂 | - | kg.cm/cm | |
洛氏硬度 | 23℃ | ASTM D-785 | 119 | 100 | R | |
洛氏硬度 | 23℃ | ASTM D-785 | 97 | - | R | |
抗拉屈服强度 | -40℃ | ASTM D-638 | 1150 | 1100 | Kg/cm2 | |
抗拉屈服强度 | 23℃ | ASTM D-638 | 800 | 530 | Kg/cm2 | |
抗拉屈服强度 | 80℃ | ASTM D-638 | 430 | 400 | Kg/cm2 | |
抗拉断裂强度 | 230℃ | ASTM D-638 | 700 | 730 | Kg/cm2 | |
断裂伸长率 | 23℃ | ASTM D-638 | 110 | < 200 | % | |
挠曲强度 | -40℃ | ASTM D-790 | 1450 | 1300 | Kg/cm2 | |
挠曲强度 | 23℃ | ASTM D-790 | 1150 | 650 | Kg/cm2 | |
挠曲强度 | 80℃ | ASTM D-790 | 640 | 400 | Kg/cm2 | |
挠曲模量 | -40℃ | ASTM D-790 | 44000 | 42000 | Kg/cm2 | |
挠曲模量 | 23℃ | ASTM D-790 | 29000 | 14000 | Kg/cm2 | |
挠曲模量 | 80℃ | ASTM D-790 | 9000 | 5000 | Kg/cm2 | |
压缩强度 | 23℃ | ASTM D-695 | 910 | - | Kg/cm2 | |
抗剪强度 | 23℃ | ASTM D-732 | 790 | 770 | Kg/cm2 | |
IZOD冲击强度 | -40℃,V缺口1/2 | --- | 3.5 | - | kg.cm/cm | |
电气性能 | 体积电阻率 | --- | ASTM D-257 | 1014-1015 | 1011-1012 | Ω.cm |
介电强度 | 1/8" | ASTM D-149 | 18 | - | KV/mm | |
介电常数 | 50HZ | ASTM D-150 | 4 | - | --- | |
介电常数 | 103Hz | ASTM D-150 | 3.9 | - | --- | |
介电常数 | 106Hz | ASTM D-150 | 3.3 | 3.8 | --- | |
损耗因素 | 50Hz | ASTM D-150 | 0.03 | - | --- | |
损耗因素 | 103Hz | ASTM D-150 | 0.03 | - | --- | |
损耗因素 | 106Hz | ASTM D-150 | 0.02 | 0.07 | --- | |
抗电弧性 | 1/8" | ASTM D-150 | 128 | - | --- | |
IEC导电径踪指数 | --- | UL 746 | ≤60 | - | V | |
热 性 能 | 线性热膨胀系数 | --- | ASTM D-696 | 9_10 | - | 10-5cm/cm |
热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 220 | - | ℃ | |
热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 220 | - | ℃ | |
UL-94抗燃级 | 1/16" | UL 94 | V-2 | - | --- | |
熔点 | --- | 差示扫描测热计DSC法 | 265 | - | ℃ | |
比热 | --- | --- | 0.4 | - | Cal/g.°C | |
导热系数 | --- | --- | 0.21 | - | Kcal/m.hr.°C |